ASTM A358/A358M
Electric-Fusion-Welded Austenitic Chromium-Nickel
Stainless Steel Pipe for High-Temperature Service
Grade:
316L, 317, 317L, 321, 321H, 348
S32050, N08800.
Welding:
The joints are full penetration bouble-welded or single-welded
Heat treatment:
All pipes are with heat treatment condition.
Please specify your heat treatment requirement in the enquiry.
Permissible Variations—The dimensions at any point in a length of pipe shall not exceed the following:
Outside Diameter—Based on circumferential measurement, 60.5 % of the specified outside diameter.
Out-of-Roundness—Difference between major and minor outside diameters, 1 %.
Alignment—Using a 10-ft [3-m] straightedge placed so that both ends are in contact with the pipe, 1⁄8 in. [3 mm] deviation from contact with the pipe.
Thickness—The minimum wall thickness at any point in the pipe shall not be more than 0.01 in. [0.3 mm] under the nominal thickness.
Table 1 Annealing Requirements
| Grade or UNS DesignationＡ | Heat Treating TemperatureＢ | Cooing/Testing Requirements |
| All grades not individually listed below: 304H,309S,309Cb,310S,310Cb,321H,347H,S22100, S28300 | 1900 °F [1040 °C] | C |
| 1900 °F [1040 °C] | D |
| N08020 | 1800-1850 °F [980-1010 °C] | D |
| N08367 | 2025 °F [1110 °C] | D |
| N08810 | 2050 °F [1120 °C] | D |
| N08904 | 2000 °F [1095 °C] | D |
| N08926 | 2010 °F [1100 °C] | D |
| S30600 | 2100 °F [1150 °C] | D |
| S30815 | 1920 °F [1050 °C] | D |
| S31254 | 2100 °F [1150 °C] | D |
| S31266 | 2100 °F [1150 °C] | D |
| S31727 | 1975–2175 °F [1080 to 1180 °C] | D |
| S32050 | 2100 °F [1150 °C] | D |
| S32053 | 1975–2175 °F [1080 to 1180 °C] | D |
| S32654 | 2100 °F [1150 °C] | D |
| S34565 | 2050 °F [1120 °C] | D |
A New designation established in accordance with Practice E527 and SAE J1086.
B Minimum, unless otherwise stated.
C Quenched in water or rapidly cooled by other means, at a rate sufficient to prevent reprecipitation of carbides, as demonstrable by the capability of passing Practices
A262, Practice E. The manufacturer is not required to run the test unless it is specified on the purchase order (see Supplementary Requirement S7). Note that Practices
A262 requires the test to be performed on sensitized specimens in the low-carbon and stabilized types and on specimens representative of the as-shipped condition for
other types. In the case of low-carbon types containing 3 % or more molybdenum, the applicability of the sensitizing treatment prior to testing shall be a matter for
negotiation between the seller and the purchaser.
D Quenched in water or rapidly cooled by other means.
Inspection and Quality Control:
In house control, also accept Customer Inspection at site or Third Party Inspection
Referenced Documents:
ASTM Standards:
ASTM A240/A240M Specification for Chromium and Chromium Nickel Stainless Steel Plate, Sheet, and Stip for Pressure Vessel and for General Application
ASTM A262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels
ASTM A480/ A480M Specification for General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and Strip
ASTM A941 Terminology Rlating to Steel, Stainless Steel, Related Alloys and Ferroalloys
ASTM A999/A999M Specification for General Requirements for Alloy and Stainless Steel Pipe
E527 Practice for Numbering Metals and Alloys (UNS)
Product Tags:
|
|
A358/A358M High Temperature Inconel Welded Stainless Steel Tube / Electric Fusion Welded Pipe Images
|